Synthesis and mechanical characterization of a non-woven nanofiber by the electrospinning technique
Síntesis y caracterización mecánica de una nanofibra no tejida por la técnica de electrohilado
DOI:
https://doi.org/10.15446/dyna.v86n209.74255Palabras clave:
nanoparticle synthesis, electrospinning, polymer cover, mechanical characterization, nanofiber, non-woven. (en)síntesis de nanopartículas, electrospinning, cubierta de polímero, caracterización mecánica, nanofibra, no tejido. (es)
Descargas
A non-woven nanofiber or polymeric cover is synthesized with nylon-6 as the base polymeric material. Different acid relationships (formic/acetic) were tested in the electrospinning equipment, until defining by macroscopic observations and SEM Scanning Electron Microscopy analysis the adequate acid ratio 3:2 and the average diameter of the nanofibers in 350nm, defining the parameters to operate the electrospinning. According to ASTM D 882 standard, the Tensile Strength was calculated for stresses applied horizontally and vertically to the direction of the nanofibers. With the standards ASTM D 7490 and ASTM G-15 the wettability was determined by measuring the contact angle, finding that it has hydrophilic properties with high wettability, adhesiveness and surface energy. Nanostructured polymer covers can be used for biological isolation in health care areas, as a protective barrier to control the spread of infections.
Se sintetiza una nanofibra no tejida o cubierta polimérica con nylon-6 como material polimérico base. Se probaron distintas relaciones ácido (fórmico/acético) en el equipo de electrospinning, hasta definir por observaciones macroscópicas y análisis de Microscopia Electrónica de Barrido SEM la relación adecuada de ácido 3:2 y el diámetro promedio de las nanofibras en 350nm, definiendo los parámetros para operar el electrospinning. Acorde a la norma ASTM D 882 se calculó la Resistencia a la Tracción para esfuerzos aplicados en sentido horizontal y en sentido vertical a la dirección de las nanofibras. Con las normas ASTM D 7490 y ASTM G-15 se determinó la humectabilidad por medición de ángulo de contacto, encontrando que tiene propiedades hidrofílicas con alta mojabilidad, adhesividad y energía superficial. La cubierta polimérica nanoestructurada puede ser usada para el aislamiento biológico en áreas de atención en salud, como barrera protectora para el control de la propagación de infecciones.
Referencias
ICONTEC, “Ntc 3911,” 1996.
N. Bhardwaj and S. C. Kundu, “Electrospinning: A fascinating fiber fabrication technique,” Biotechnol. Adv., vol. 28, no. 3, pp. 325–347, 2010.
K. Molnár and B. Farkas, “Electrospun Nanofibers for Textile Application - a Finite Element Study,” COMSOL Conf., 2015.
Li. Yan, H. Zhengming, L. Yandong. "Electrospinning of nylon-6,66,1010 terpolymer" POLYMER,” vol. 42, pp. 1696–1704, 2006.
L. Francis, F. Giunco, A. Balakrishnan, and E. Marsano, “Synthesis , characterization and mechanical properties of nylon – silver composite nanofibers prepared by electrospinning,” Curr. Appl. Phys., vol. 10, no. 4, pp. 1005–1008, 2010.
M. L. Mejía et al., “Properties of Antibacterial Nano Textile for Use in Hospital Environments,” pp. 13–19, 2017.
“Poliamida - Nylon.” [Online]. Available: http://www.ensinger.es/es/materiales/plasticos-de-ingenieria/poliamida/. [Accessed: 28-Nov-2017].
Yeum Jeong Hyun, Park Jae Hyeung, and Choi Jae Young, “Polymer / montmorillonite / silver prepared by in-situ polymerization and electrospraying technique,” Intech, pp. 165–187, 2006.
ASTM International, “ASTM D882: Standard Test Method for Tensile Properties of Thin Plastic Sheeting,” ASTM Stand., p. 12, 2012.
ASTM, “Standard D7490--13 Standard Test Method for Measurement of the Surface Tension of Solid Coatings, Substrates and Pigments using Contact Angle Measurements,” Astm, pp. 1–5, 2013.
Á. Rodríguez, “Estudio del ángulo de contacto y de la mojabilidad a alta temperatura de fases líquidas en la sinterización de metales,” p. 114, 2010.
Cómo citar
IEEE
ACM
ACS
APA
ABNT
Chicago
Harvard
MLA
Turabian
Vancouver
Descargar cita
Licencia
Derechos de autor 2019 DYNA
Esta obra está bajo una licencia internacional Creative Commons Atribución-NoComercial-SinDerivadas 4.0.
El autor o autores de un artículo aceptado para publicación en cualquiera de las revistas editadas por la facultad de Minas cederán la totalidad de los derechos patrimoniales a la Universidad Nacional de Colombia de manera gratuita, dentro de los cuáles se incluyen: el derecho a editar, publicar, reproducir y distribuir tanto en medios impresos como digitales, además de incluir en artículo en índices internacionales y/o bases de datos, de igual manera, se faculta a la editorial para utilizar las imágenes, tablas y/o cualquier material gráfico presentado en el artículo para el diseño de carátulas o posters de la misma revista.