Annealing efficacy on PLA. Insights on mechanical, thermomechanical and crystallinity characters
Efectividad de recocido en PLA. Información sobre las propiedades mecánicas, termomecánicas y de cristalinidad
Keywords:
PLA, annealing, crystallinity, properties (en)PLA, recocido, cristalinidad, propiedades (es)
Downloads
Poly (lactic acid) (PLA) is widely used biodegradable thermoplastic in the additive manufacturing, mainly on manufactured products through 3D printing. However, PLA is highly fragile and presents low impact strength; hence improvements on this way are industrially and technologically important. Aiming to develop proper methodology for higher PLA performance, this work investigated the effects of thermal annealing on the mechanical properties (impact, tensile, Shore D hardness), heat deflection temperature (HDT), Vicat softening temperature (VST) and crystallinity (X-ray diffraction) of PLA. Injected specimens were annealed in greenhouses at 70, 80, 90 and 100 °C. Annealing at 70 °C was not effective, without verified significant changes. On the other hand, annealing at 80, 90 and 100 °C provided crystalline peaks in DRX, indicating development of structural organization. Expressive results were achieved, at 90 °C, for impact strength, HDT, VST, Shore D hardness and tensile strength, related to non-annealed PLA. Provided results in this work have scientific and technological importance, since the mechanical and thermomechanical properties of PLA were improved using a simple methodology which may render higher performance products mainly for the 3D printing industry of PLA.
El poli (ácido láctico) (PLA) es un termoplástico biodegradable ampliamente utilizado en la fabricación de aditivos, principalmente en productos fabricados mediante impresión 3D. Sin embargo, el PLA es muy frágil y tiene baja resistencia al impacto; por lo tanto, las mejoras en este sentido son industrial y tecnológicamente importantes. Con el fin de desarrollar una metodología adecuada para un PLA de mayor rendimiento, este trabajo investigó los efectos del recocido térmico en las propiedades mecánicas (impacto, tracción, dureza de la Shore D), temperatura de desviación térmica (HDT), temperatura de ablandamiento de Vicat (TAV) y cristalinidad (difracción de rayos X) del PLA. Las muestras inyectadas fueron recocidos en horno a 70, 80, 90 y 100°C. El recocido a 70 ° C no fue efectivo, sin cambios significativos verificados. Por otro lado, el recocido a 80, 90 y 100 ° C proporcionó picos cristalinos en la DRX, lo que indica el desarrollo de la organización estructural. Los resultados expresivos se lograron a 90°C para resistencia al impacto, HDT, VST, dureza Shore D y resistencia a la tracción, relacionados con PLA sin recocido. Los resultados presentados en este trabajo son de importancia científica y tecnológica, ya que las propiedades mecánicas y termomecánicas del PLA se han mejorado utilizando una metodología simple que puede producir productos de mayor rendimiento principalmente para la industria de impresión 3D de PLA.
Downloads
References
M. Okan, H. M. Aydin, and M. Barsbay, J. Chem. Technol. Biotechnol. 94, 8 (2019).
C. B. B. Luna, D. D. Siqueira, E. da Silva Barbosa Ferreira, E. M. Araújo, and R. M. R. Wellen, Mater. Res. Express 6, 125317 (2019).
F. G. Torres, S. Rodriguez, and A. C. Saavedra, J. Polym. Environ. 27, 2651 (2019).
D. D. Siqueira, C. B. Luna, E. M. Araújo, D. D. S. M. E. A. S. Filho, and R. M. R. Wellen, Mater. Res. 22 (2019).
MATWEB, Blendas pla/pegaa: Avaliacao da reatividadeentre os polímeros e da concentracao de pegaa nas propriedades e na morfologia," (Consultada el 10 de mayo de 2020).
N. Eselini, S. Tirkes, A. O. Akar, and U. Tayfun, J. Elastomers Plast. 52, 701 (2020).
E. Teoh and W. Chow, J. Elastomers Plast. 50, 596 (2018).
V. G. Gokhare, D. N. Raut, and D. K. Shinde, A review paper on 3d-printing aspects and various processes used in the 3d-printing," (2017).
G. F. Brito, P. Agrawal, E. M. Araujo, and T. J. A. Melo, Polímeros 23, 531 (2013).
F.-C. Pai, H.-H. Chu, and S.-M. Lai, J. Elastomers Plast. 52, 53 (2020).
J. C. C. Lima, P. A. E. A. G. Araújo, and T. J. A. Mélo, Macromol. Symp. 383, 1700072 (2019).
K. Belkouicem, A. Benarab, R. Krache, R. Benavente, E. Pérez, and M. Cerrada, J. Elastomers Plast. 51, 562 (2019).
T. Takayama, M. Todo, and H. Tsuji, J. Mech. Behav. Biomed. 4, 255 (2011).
R. J. Xu, X. D. Chen, Q. Cai, C. B. Chen, Y. F. Lin, C. H. Lei, and L. B. Li, RSC Adv. 5, 27722 (2015).
T. Tábi, I. E. Sajó, F. Szabó, A. S. Luyt, and J. G. Kovács, Express Polym. Lett. 4, 659 (2010).
Y. Srithep, P. Nealey, and L. S. Turng, Polym. Eng. Sci. 53, 580 (2013).
R. B. Pereira and A. R. Morales, Polímeros 24, 198 (2014).
J. F. Mano, Y. Wang, J. C. Viana, Z. Denchev, and M. J. Oliveira, Macromol. Mater. Eng. 289, 910 (2004).
M. L. Di Lorenzo, M. Cocca, and M. Malinconico, Thermochim. Acta 522, 110 (2011).
W. D. Callister., Ciencia e engenharia de materiais uma introducao. 7 ed. (LTD, 2011).
E. B. Bezerra, D. C. Franca, D. D. d. S. Morais, D. D. Siqueira, E. M. Araújo, and R. M. R. Wellen, REM: Int. Eng. J. 72, 469 (2019).
J. C. C. Lima., Blendas de poli(ácido lático) com copolímero tribloco de estireno/etileno-butileno/estireno (Dissertacao de mestrado). (Campina Grande: Departameno de Engenharia de Materiais, Univesidade Federal de Campina Grande, 2016) pp. 1-125.
M. Pastorek and A. Kovalcik, Mater. Manuf. Process. 33, 1674 (2018).
M. Pastorek and A. Kovalcik, Mater. Manuf. Process. 33, 1674 (2018).
S. D. Park, M. Todo, and K. Arakawa, J. Mater. Sci. 261, 105 (2004).
H. T. Oyama, Polymer 50, 747 (2009).
L. Yu, H. Liu, F. Xie, L. Chen, and X. Li, Polym. Eng. Sci. 48, 634 (2008).
S. Park, M. Todo, and K. Arakawa, J. Mater. Sci. 39, 1113 (2004).
C. B. B. Luna, E. da Silva Barbosa Ferreira, D. D. Siqueira, W. A. da Silva, E. M. Araujo, and R. M. R. Wellen, Mater. Res. Express 6, 115321 (2019).
E. B. Bezerra, D. C. d. Franca, D. D. d. S. Morais, I. D. d. S. Silva, D. D. Siqueira, E. M. Araujo, and R. M. R. Wellen, Polímeros 29 (2019).
D. D. d. S. Morais, D. C. Franca, E. M. Araújo, L. H. d. Carvalho, R. M. R. Wellen, A. D. d. Oliveira, and T. J. A. d. Melo, REM: Int. Eng. J. 72, 87 (2019).
M. S. Rabello and J. R. White, Polímeros 7, 47 (1997).
D. Wright, R. Dunk, D. Bouvart, and M. Autran, Polymer 29, 793 (1988).
M. Gahleitner, K. Bernreitner, W. Nei l, C. Paulik, and E. Ratajski, Polym. Test. 14, 173 (1995).
C. B. B. Luna, D. D. Siqueira, E. M. Araújo, and R. M. R. Wellen, Mater. Res. Express 6, 075316 (2019).
A. M. Harris and E. C. Lee, J. Appl. Polym. Sci. 107, 2246 (2008).
G. Perego and G. D. Cella, Mechanical properties," in Poly(Lactic Acid) (John Wiley & Sons, Ltd, 2010) Chap. 11, pp. 141-153.
License
Copyright (c) 2020 MOMENTO
This work is licensed under a Creative Commons Attribution-NoDerivatives 4.0 International License.
Those authors who have publications with this journal, accept the following terms:
a. The authors will retain their copyright and will guarantee the publication of the first publication of their work, which will be subject to the Attribution-SinDerivar 4.0 International Creative Commons Attribution License that permits redistribution, commercial or non-commercial, As long as the Work circulates intact and unchanged, where it indicates its author and its first publication in this magazine.
b. Authors are encouraged to disseminate their work through the Internet (eg in institutional telematic files or on their website) before and during the sending process, which can produce interesting exchanges and increase appointments of the published work.